15 MeV proton damage in NiO/β-Ga2O3vertical rectifiers

Abstract 15 MeV proton irradiation of vertical geometry NiO/β-Ga2O3heterojunction rectifiers produced reductions in reverse breakdown voltage from 4.3 kV to 3.7 kV for a fluence of 1013ions·cm−2and 1.93 kV for 1014ions·cm−2. The forward current density was also decreased by 1–2 orders of magnitude under these conditions, with associated increase in on-state resistanceRON. These changes are due to a reduction in carrier density and mobility in the drift region. The reverse leakage current increased by a factor of ∼2 for the higher fluence. Subsequent annealing up to 400 °C further increased reverse leakage due to deterioration of the contacts, but the initial carrier density of 2.2 × 1016cm−3was almost fully restored by this annealing in the lower fluence samples and by more than 50% in the 1014cm−2irradiated devices. Carrier removal rates in the Ga2O3were in the range 190–1200 for the fl…