Ultrahigh Deep-UV Sensitivity in Graphene-Gated β-Ga2O3 Phototransistors

Deep-ultraviolet (UV) photodetectors based on ultrawide bandgap β-Ga 2 O 3 have a great potential in civil or military applications especially due to its inherent solar-blindness. Metal–semiconductor phototransistors based on exfoliated β-Ga 2 O 3 were fabricated using graphene as a highly transparent gate electrode. Controlling the potential barrier at the metal–semiconductor junction through the UV-transparent graphene gate expanded the difference between the UV-illuminated current and the dark current. Therefore, the photo-to-dark current ratio (PDCR) was raised by 6 orders of magnitude under the optimal gate bias. The performances of β-Ga 2 O 3 phototransistors were exceptionally superior among the deep-UV photodetectors based on wide bandgap semiconductor materials; PDCR of 6.0 × 10 8 and rejection ratio of 5.3 × 10 6 could be achieved. The synergetic combination of an ultrawide ban…