Healing of Microdefects in SSZ-13 Membranes via Filling with Dye Molecules and Its Effect on Dry and Wet CO2 Separations

It is quite challenging to avoid microdefect formation during hydrothermal growths and/or calcination processes, while manufacturing high-quality zeolite membranes in a reproducible manner. Even less than 1% of defects, which generally provide nonselective pathways, will considerably worsen the intrinsic, high molecular sieving-based separation performance of a continuous zeolite membrane. Herein, we propose a simple and reliable method for blocking defects using water-soluble dye molecules, which were originally used for the visualization of nonzeolitic, defective structures in a zeolite membrane. Because the dye molecules are ∼1 nm in size, they cannot diffuse into the zeolitic pores and selectively access the defects. For the demonstration of dye-based defect healing, we chose a siliceous chabazite type SSZ-13 zeolite membrane (pore size = 0.37 × 0.42 nm 2 ) with some degree of defect…