Revealing the Nanoscopic Corrosive Degradation Mechanism of Nickel-Rich Layered Oxide Cathodes at Low State-of-Charge Levels: Corrosion Cracking and Pitting

Ni-rich layered oxides have received significant attention as promising cathode materials for Li-ion batteries due to their high reversible capacity. However, intergranular and intragranular cracks form at high state-of-charge (SOC) levels exceeding 4.2 V (vs. Li/Li + ), representing a prominent failure mechanism of Ni-rich layered oxides. The nanoscale crack formation at high SOC levels is attributed to a significant volume change resulting from a phase transition between the H2 and H3 phases. Herein, in contrast to the electrochemical crack formation at high SOC levels, another mechanism of chemical crack and pit formation on a nanoscale is directly evidenced in fully lithiated Ni-rich layered oxides (low SOC levels). This mechanism is associated with intergranular stress corrosion cracking, driven by chemical corrosion at elevated temperatures. The nanoscopic chemical corrosion behavi…